Materials
From Raw to Finished Products
We are able to manipulate and process a variety of the most commonly used materials in the manufacture of industrial and consumer parts, components and products for aluminum alloy casting, bronze casting, stainless steel precision casting. To achieve the high standards that all of our clients expect from us, we start with selecting only the finest raw materials, carefully inspected for flaws or defects.
Aluminum Alloy
Alloy |
Heat Treatment |
TS (kpsi) |
YS (kpsi) |
% Elongation |
Hardness |
|---|---|---|---|---|---|
A356.2 |
Solution + Aging |
35 Min |
24 Min |
3.5 Min |
HRB 45 -55 |
Stainless Steel
300 Series
|
Heat Treatment |
TS (kpsi) |
YS (kpsi) |
% Elongation |
Hardness |
|---|---|---|---|---|---|
303 (CF16Fa8) |
Annealing |
70 Min |
30 Min |
25 Min |
HRB 95 Max |
304 (CF8) |
Annealing |
70 Min |
30 Min |
35 Min |
HRB 95 Max |
316 (CF8M) |
Annealing |
70 Min |
30 Min |
30 Min |
HRB 95 Max |
316L (CF3M) |
Annealing |
70 Min |
30 Min |
30 Min |
HRB 95 Max |
400 Series |
|||||
410 (CA-15) |
Quenching + Tempering |
90 Min |
65 Min |
18 Min |
HRC 28 – 45 |
600 Series |
|||||
630 (17-4PH) |
Solution |
150 Min |
110 Min |
13 Min |
HRC 36 Max |
630 (17-4PH) |
Soultion + Aging |
180 Min |
160 Min |
6 Min |
HRC 39 Min |
Nickel Alloy |
|||||
Monel 400 (M30C) |
As Cast |
65 Min |
32.5 Min |
25 Min |
HRC 60 – 80 |
Copper Alloy
Low Lead
|
Heat Treatment |
TS (kpsi) |
YS (kpsi) |
% Elongation |
Hardness |
|---|---|---|---|---|---|
C87850 |
Not Applicable |
65 Min |
25 Min |
8 Min |
Not Applicable |
Nickel Aluminum
|
|||||
C95800 |
Annealing |
85 Min |
35 Min |
15 Min |
HRB 95 Max |